摘要：装饰性镀层由于其鲜艳的外观而日益受到人们的青睐。为提高装饰性镀层的耐蚀性，延长其使用寿命，开发出一种无色透明涂膜。该涂膜由新型改性聚合物树脂和多种助剂组成，具有良好的耐磨、抗蚀及抗紫外线照射性能，工艺简单，可广泛用于镀层的表面防护与装饰。
　　关键词：无色透明涂膜　耐磨　抗蚀

Studies on the Process of Wear-Resistance, Anticorrosive,
Achromatic Transparent Coating and Its Application

MA Pingxiang　ZHANG Yuanming

Abstract:Decorative coatings are becoming increasingly popular for their bright colored appearance. The purpose of the study was to improve the corrosion resistance of decorative coatings. A new achromatic transparent coating was developed which consists of polymer-modified resin and some auxiliaries. The process is simple with strengths such as good wearability, corrosion resistance, and resistance to irradiation of ultraviolet, and can be extensively used in preventive and decorative coatings.
Keywords:achromatic transparent coating, wear-resisting, anticorrosive

1　前言

　　随着人民生活水平的不断提高，对装饰品的要求越来越高，许多商场、宾馆的门面装饰、钟表、镜框、灯具等的表面着色，五彩缤纷，鲜艳夺目。这些色彩以金黄为主，也有仿古铜，黑色、银白色等。获得色彩的方法有电镀、真空镀、阳极氧化、电泳等。然而，这些装饰品长期暴露在空气中，与氧、硫等作用，有的还在室外受紫外线的直接照射，漂亮的外观色彩难于持久，为了延长这些装饰品的使用时间，笔者经多年的试验和研究，开发出一种新型的无色透明涂膜。

2　配方及涂膜性能

　　该涂料由基料、整平剂、抗氧剂、抗紫外线剂等组成。性能良好，适用范围广。
2.1　基料
　　基料是涂料的成膜物质，是整个耐磨、抗蚀涂料的骨架，没有它，涂料就不可能形成一层连续的涂膜。
　　目前，用于保护性涂料的有丙烯酸树脂、环氧树脂、聚氨酯树脂和有机硅树脂的清漆或烘漆。笔者通过对比和筛选试验，研制出一种具有室温固化、附着力好、光泽度高、耐磨、耐水的改性丙烯酸树脂，其主要性质见表1。

表1　涂料及涂膜的主要性质